Antifouling ALU PLUS

It is designed for use on aluminum, steel, laminate, and wood.

ColorCapacityCode
white750 ml / 2,5 l5859 / 5861
navy / blue750 ml / 2,5 l8026 / 8027
black750 ml / 2,5 l8029 / 8030
Antifouling ALU PLUS

Technical informations

Color

Exposure of a freshly applied antifouling paint to moist air can lead to color change. The discoloration is only superficial and does not affect the effectiveness of the antifouling paint.

Product removed from offer 1 March 2022.

Application method

Manually:

  • brush
  • roller

Spray:

  • airless spray

Product description "Antifouling ALU PLUS"

  • Self – polishing Antifouling ALU PLUS protect areas below the water line.
  • It can be applied on aluminium (light alloy), steel, wood, fiberglass hulls.
  • It is suitable for light alloy (aluminium) hulls. No risk of galvanic corrosion on aluminium surfaces.
  • Suitable for all kind of boats up to 40 knots of speed.
  • Recommended for salt and sweet water.
  • Extremely effective, very high performance.
  • 30% higher output than regular antifouling paint.
  • Easy to apply.
  • Fast drying time.
  • Thinning is not recommended because it reduces the effectiveness of the paint.
  • As a primer coat, use Sea-Line® epoxy primer  – for example:  Sea-Line® Anticorossion preotection 4:1, Lightprimer 5:1, Universal primer 1K.

Basic information

Typealuminum, GRP laminates, wood, steel
PlaceBelow waterline
FunctionAntifouling paint discourages the growth
of barnacles, weed, and
Applicationbrush, roll, spray gun other water life
on the submersed hull of the boat.
Thinning**No recomended
Theoretical coverage For 1l11 m2 for
90 μmWFT/ 50 μm DFT
Coats number1 – 3
Pot life 20°CMin 5 h – max 7 days
Time between layers without sandingMin 12 h – max 6 months

You have questions about the product - Antifouling ALU PLUS

    Thinning notice:

    In the case of high temperatures and the need to thin the antifouling paint, a maximum dilution of 0-5% (by volume) is recommended.
    Dilution and the application method directly affect the thickness of the antifouling paint layer.

    Special attention should be paid to obtaining a specific coating thickness (100 μm DTF), which ensures the effective operation of the antifouling paint.

    Also check

    Our FAQ answers to frequently asked questions

    Why does the paint have no adhesion?

    Possible causes

    • Wrong surface preparation,
    • Skipping the primer in the system application process,
    • Use of universal thinners or replacements ,
    • Paint incompatibility.

    How to prevent

    • Correct surface preparation (grinding, clearing, degreasing),
    • Use primers which improve adhesion of paints,
    • Use thinners which are dedicated to each paints,
    • Use of paints which are compatible to each other.

    How to remove

    • Grind, clean and paint again.

    Contamination in topcoat paint?

    Possible causes

    • Inaccurate surface cleaning before paint application,
    • Incorrect painting tools preparation (brush and roll),
    • Performing work in a place exposed to constant contact with dust.

    How to prevent

    • Careful surface preparation (grinding, clearing, degreasing),
    • Careful painting tools preparation before use,
    • Maintain clean work environment

    How to remove

    • Grind, clean and paint again.

    Can I use selfpolishing Sea-Line and HARD Sea-Line antifoulings on aluminium boat?

    Sea-Line HARD and Sea-Line self-polishing antifouling are not intended for aluminum surfaces. They include copper oxide, which in contact with aluminum causes galvanic corrosion. Especially on aluminum, we offer ALU-PLUS self-polishing anti-fouling paint, which, in addition to excellent adhesion to aluminum, is also 30% more effective than traditional anti-fouling paints.