Use biocides safely. Always read the label and product information before use.
| Type | GRP laminates, wood, steel | |||||
| Place | Below waterline | |||||
| Function | Antifouling paint discourages the growth of barnacles, weed, and other water life on the submersed hull of the boat. | |||||
| Application | brush, roll only professional : airless spray gun or conventional spray | |||||
| Thinning * | No recommended | |||||
| Theoretical coverage For 1l | by roller | by spray | ||||
| 11 ~ 12 m² | 4 ~ 6 m² | |||||
| Coat thickness (WTF) | 80 μm | 160 μm | ||||
| Finish thickness (DTF) | 30 μm | 60 μm | ||||
| Coats number | 2 | 1 | ||||
| Recommended dry layer | 60 μm | |||||
| Hardening the surfaces | 23ºC | 15ºC | ||||
| Touch dry | 20 minutes | 30 minutes | ||||
| Immersion: | 2 hours | 3 hours | ||||
| Dry to recoat (overcoating) | min. 6 hours | min. 10 hours | ||||
| Dry to launch (immersion times) | max 6 months | max 6 months | ||||
| Pack | 0,75 l | 2,0 l | ||||
| Color | code | code | ||||
| Graphite | 300008380 | 300008379 | ||||
In the case of high temperatures and the need to thin the antifouling paint, a maximum dilution of 0-5% (by volume) is recommended.
Dilution and the application method directly affect the thickness of the antifouling paint layer.
Special attention should be paid to obtaining a specific coating thickness (100 μm DTF), which ensures the effective operation of the antifouling paint.
Silver Speed HARD Antifouling is a hard antifouling paint, effectively preventing fouling organism: aquatic plants and animals or slime. Ideal […]
HARD ANTIFOULING paint: Suitable for salty and regular water. Suitable for sailing and motor boats traveling with a maximum speed […]
Silver Cruise Polishing Antifouling it’s effectively preventing fouling organism: aquatic plants and animals or slime. Ideal paint for professional and […]
PENNELLO PROFESSIONALE Sea-Line® PENNELLO Sea-Line® RULLI Sea-Line® IMPUGNATURA PER RULLI Sea-Line® VASCHETTA PLASTICA Sea-Line® STECCA PER MISCELARE Sea-Line® TAZZE GRADUATE […]
No, polyurethane is a 2-component paint (base + hardener) and after applying 2-component paint to 1-component paint, the proper adhesion of the paint to the surface will not be maintained, the paint will begin to wrinkle and surface defects will appear.
Il patch e compensare le irregolarità derivanti da danni durante la produzione
Barca protezione superficiale contro l’influenza di azioni distruttive di osmosi e la corrosione in ambienti difficili
Protezione contro l’acqua e contro gli effetti negativi delle radiazioni UV
Proteggere la parte inferiore della barca prima-tedesco ricoperta di alghe e conchiglie. La prevenzione dell’azione di acqua.
Rimozione efficace di ritenzione graffi, di aggiornamento e il colore del mantello gel o lacca
Laminazione, incollaggio e tappatura perdite
Per il riempimento di piccole fessure e ubyt gemme in gelcoat
Una gamma di prodotti utili quando si lavora costruttore di barche